INDEX

SURFACE CONDITIONING

  • Alkaline soak Cleaners
  • Alkaline Electrolytic cleaners
  • Electrolytic Alkaline De-rusting
  • Spray cleaners

ACID PICKLING & BRIGHTENING

COPPER PLATING

  • Cyanide Copper
  • Bright Acid Copper

NICKEL PLATING PROCESS

  • Bright
  • Duplex & Triplex
  • Satin

ELECTROLESS NICKEL

NICKEL-FREE PLATING PROCES

  • WHITE BRONZE
  • GOLDEN YELLOW BRONZE
  • ANTIQUE BRONZE

CHROME PLATING PROCESS

TIN-COBALT PROCESS (CHROMELIKE)

ZINC PLATING

  • Cyanide
  • Acid
  • Alkaline Non-cyanide

CHROMATE CONVERSION COATING & SEALANTS

ORGANIC PROTECTIVE COATINGS

TIN & TIN LEAD ALLOY PLATING

SILVER PLATING

GOLD PLATING

BRIGHT CADMIUM PLATING

BRASS PLATING PROCESS

METAL STRIPPERS

BLACKENING & COLOURING

PLATING ON ALUMINIUM

ELECTROPHORETIC COATINGS

PHOSPHATE COATINGS

ANODIZING

BASIC CHEMICALS

SURFACE CONDITIONG
ALKALINE SOAK CLEANERS / FERROUS / NON-FERROUS

PROCESS

/ COMPOSITION OPERATING CONDITIONS / APPLICATIONS AND Features
CLEANER MS-120-R
SK-140 / MS-120R/SK-140 / 45-65 G/L
65-800C
2-5 MINS / 25-30 G/L
65-800C
2-5 MINS / Heavy duty alkaline soak cleaner for ferrous and non ferrous metals can be use as electro cleaner also..
CLEANER MK-20 / CLEANER-
MK-20
Temperature
Time / 45-65 g/l
ROOM
2-5 Mins / 30-50 g/l
ROOM
2-5 Mins / Specially developed for use in energy conserving systems. suitable for ferrous metals
CLEANER-ME-112 / CLEANER-
ME-112
CAUSTIC SODA
(OPTIONAL)
TEMPERATURE
CURRENT DENSITY / 20-50 g/l
10-20 g/l
65-850C
1-4A/dm2 / 20-50 g/l
--
60-700C
---- / high effficiency cleaner suitable for ferrous and non-ferrous metals including zinc base diecasting.
  • deisigned for use as soak and electrolytic cleaner.
  • excellent emulsifying power and has a longer bath life.

CLEANER-ME-119 / CLEANER-ME119
SODIUM
HYDROXDE
TEMPERATURE
TIME / 50-100 ml/l
20-60 g/l
80-900C
2-5 Mins / 50-100 ml/l
---
60-700C
2-4 mins /
  • a versatile liquid soak cleaner used along with sodium hydroxide for efficient soak cleaning of steel.
  • can replace solvent cleaning hence economical process.

CLEANER
MSE-111 / CLEANER-
MSE-111
TEMPERATURE
TIME / 50-80 g/l
ROOM –800C
2-5 MINS / 25-30 g/l
ROOM –800C
2-5 MINS /
  • heavy duty alkaline soak cleaner for ferrous and non-ferrous metals.
  • cleaner is designed for heavy oil and soil removal in short time
  • solution is very clean even after prolonged working.

ALKALINE ELECTROLYTIC CLEANER

PROCESS / COMPOSITION OPERATING CONDITIONS / APPLICATIONS AND Features
CLEANER-112 SPL / CLEANER-112 SPL TEMPERATURE TIME
CURRENT DENSITY / 60-90 G/L
65-700C
2-5 MINS
5-10 A/dm2 /
  • heavy duty chelated alkaline cleaner for ferrous metals.
  • can be used as a cathodic cleaner for activating passive nickel electrodeposit.

CLEANER
MENF-113 / CLEANER-MENF-113
TEMPERATURE
TIME
CURRENT
DENSITY / 50-60 g/l
70-800C
1-2 MINS
2.5-5 A/dm2 /
  • Chelated electro cleaner for brass and copper alloys.
  • Very good cleaning action

CLEANER-ME-119 / CLEANER-ME-119
TEMPERATURE
TIME
CURRENT DENSITY / 30-45 g/l
60-700C
2-5 MINS
1-4 A/dm2 /
  • Used as a soak electrolytic cleaner on variety of metals. ideal for zinc base diecasting and brass parts.

CLEANER MSE-011 / CLEANER-MSE-011 TEMPERATURE TIME
CURRENT DENSITY / 60-80 G/L
75-900C
1-5 MINS
5-10 A/dm2 /
  • A high current density electrolytic cleaner for rapid removal of smut and light rust, soil from steel.
  • Good substitute for anodic acid etch prior to nickel plating

CLEANER-113 BC / CLEANER-113BC
TEMPERATURE
TIME
CURRENT
DENSITY / 30-60 g/l
40-500C
30SECS.-3 MINS
1.3.5 A/dm2 /
  • Good cathodic cleaner for copper and brass
  • Can also be effectively used as a anodic cleaner for copper and brass

ELECTROLYTIC ALKALINE DERUSTING

PROCESS / COMPOSITION OPERATING CONDITIONS / APPLICATIONS AND Features
RUST CLEAN MS130 / RUST CLEAN-MS-130 TEMPERATURE TIME
CURRENT DENSITY / 120-180 G/L
ROOM
2-5 MINS
5-10 A/dm2 /
  • An electrolytic scale and rust remover.
  • Very good substitute for anodic acid etches.
  • Very good cleaner prior to electroless nickel on steel.
  • Non-cyanide cleaner.

RUST CLEANER-MS-131 / RUST CLEAN-MS131
TEMPERATURE
TIME
CURRENT
DENSIT / 180-360 g/l
ROOM
2-5 MINS
5-10 A/dm2 /
  • An efficient electrolytic scale and rust remover. since it contains cyanide, thick scales can be removed very efficiently
  • Ideal for use as a periodic reverse cleaner.

SPRAY CLEANER

CLEANER SP-120 / CLEANER SP-120 TEMPERATURE SPRAY PRESSURE
TIME / 15-30 G/L
60-900C
15-30 PSI
AS PER REQUIREMENT /
  • Heavy duty chelated alkaline cleaner for ferrous metals.

ACID PICKLING & BRIGHTENING

MAHAPICK-07 / NITRIC ACID
SULPHURIC ACID
WATER
MAHAPICK-07
TEMPERATURE
TIME / 400 ML
250 ML
250 ML
120 GMS.
ROOM
5-15 SECS /
  • Supplied in a powder form, which replaces hazardous hydrofluoric acid and hence easy to handle
  • Added to the acid dip prior to plating to remove siliceous film and thus ensured adherent haze free deposits.
  • Also used as an additive to sulphuric, nitric pickling baths and smut removal for aluminium alloys, stainless steel and titanium.

MAHAPICK-30 / MAHAPICK-30
TEMPERATURE
TIME / 30-50 G/L
ROOM
10-20 SECS. /
  • A dry acid salt used for making acid dips for removal of silicate and oxide films from ferrous and non ferrous metals to get better adhesion of subsequent electrodeposits.

ACID INHIBITOR / ACID INHIBITOR
HYDROCHLORIC ACID TEMPERATURE / 10-20 ML/L
20-30 % BY VOL.
ROOM /
  • An excellent inhibitor specially developed for hydrochloric acid, sulphuric acid picking bath for steel to reduce the base metal attack during picking. Suitable before nickel plating.

ACID INHIBITOR-SPL / ACID INHIBITOR-SPL
HYDROCHLORIC ACID TEMPERATURE / 10-20 ML/L
20-30 % BY VOL.
ROOM /
  • An execellent inhibitor specially developed for hydrochloric acid, sulphuric acid pickling bath for steel to reduce the base metal attack during picking. Suitable before nickel plating.

MAHATEK-222
ACCELERATOR
(PICKLE AID) / MAHATEK-222 ACCELERATOR
HYDROCHLORIC ACID / 30.0-60.0 G/L
30-50% BY VOL /
  • Aids in improving the tough scale in pickling bath.

MAHATEK-
MZ-052 / MAHATEK MZ-052
TEMPERATURE
TIME / 300 ml/l
60-650C
10-45 secs. /
  • Brightening dip for mazak based components.
  • Zinc diecasting parts are brightened without attacking the base metal
  • Smoothens the component and thus can produce glossy finish

BRASSBRITE-DIP
PROCESS / BRASSBRITE -DIP
HYDROGEN PEROXIDE(35%)
TEMPERATURE
TIME / 50-100 ml/l
100 ml/l
30-500C
1-10 mins. /
  • Brightening dip for brass & copper components.
  • Smoothens the component and thus
Can produce glossy finish
  • A dip in 5% sulphuric acid is used after brassbrite-dip to get a glossy finish.

COPPER PLATING PROCESS

CYANIDE COPPER
CYNO COPPER SALT-1150 / CYNO- COPPER SALT 1150
TEMPERATURE
CURRENT DENSITY / 75-150 g/l.
45-50oC
1-2 A/dm2 /
  • General purpose cyanide copper plating bath to produce light as well as heavy deposits.
  • Produces smooth semibright copper deposits suitable for vat and barrel plating.

CYNO ROCHELLE COPPER SALT 1160 / CYNO-ROCHELLE COPPER SALT1160
TEMPERATURE
CURRENT DENSITY / 150-250 g/l.
45-50oC
2-3 A/dm2 /
  • Produces smooth deposits
  • Ideally suitable for zinc base diecastings.

CYNO SUPER COPPER SALT –1150 / CYNO SUPER COPPER SALT1150
COPPER ADDITIVE
COPPER BRIGHTNER TEMPERATURE
CURRENT DENSITY / 200 G/L
30-40 G/L
2-4 ML/L
45-60oC
3-5 A/dm2 /
  • Produces smooth bright deposits specially used for high current density operations.
  • Ideal product for copper plating on steel to be used for case hardening application
  • Best product for barrel plating on zinc base diecase components.

BRIGHT ACID COPPER
MARWELL-1180 / COPPER SULPHATE
SULPHURIC ACID
MARWELL BRIGHTNER-1180
MARWELL ADDITIVE-1181
CHLORIDE
TEMPERATURE
CURRENT DENSITY / 175-250 G/L
25-35 ML/L
4-8 ML/L
0.4-1.2ML/L
80-100 PPM
20-35oC
2-6 A/dm2 /
  • Process has wide brightness range, especially at extreme low current density area for plating on zinc diecasting, steel aluminium etc.
  • Has a wide useful operating range, so the solution control is very easy.
  • The bath can be operated at wide bath temperature range 20-35oc
  • Good brightness and levelling
  • Good throwing power.

NICKEL PLATING PROCESS

BRIGHT NICKEL
BRIGHT NICKEL
607/033 / SUPER BRIGHT NICKEL SALT531R
NI- ADDITIVE 602
BRIGHTNER-607/033
TEMPERATURE
PH
CATHODE CURRENT DENSITY / 350-400 G/L
8-10 ML/L
0.2-0.3 ML/L
55oC
4.2-4.6
3.0-4.0 A/dm2 /
  • An ultra high performance economical bright nickel system with exceptional good levelling, brightness and chrome receptivity.
  • Specially recommended for use in part of duplex nickel system for automatic plating installations
  • Low brightener consumption and hence becomes an economical process

BRIGHT NICKEL
677M PROCESS / SUPER BRIGHT
NICKEL SALT531R
NI ADDITIVE 602/622
NICKELBRIGHTENER-677M
TEMPERATURE
PH
CATHODE CURRENT DENSITY / 350-400 G/L
8-10 ML/L
0.2-0.3 ML/L
55oC
4.2-4.6
3.0-4.0 A/dm2 /
  • A high performance additions agent system formulated to give highest degree of levelling, brightness, coverage and chrome receptivity.
  • Suitable for vat and barrel plating
  • Very fast brightening and levelling properties.

ROSHNI BRIGHT NICKEL
786 PROCESS / SUPER BRIGHT
NICKEL SALT531R
ROSHNI ADDITIVE 786/022
ROSHNI BRIGHTNER786
ANTIPIT A (OPTIONAL)
TEMPERATURE
PH
CATHODE CURRENT DENSITY / 300-400 g/l
8-10 ML/L
0.2-0.3 ML/L
50-65oC
4.2-4.6
2.0-4.0 A/dm2 /
  • Designed primarily for duplex nickel system where 786 brightner nickel is used for depositing highly levelled ductile deposit over (sulphur free) semi bright nickel coating.
  • Very good coverage even at very low c.d areas.
  • Trouble free bright nickel process
  • Excellent chrome receptivity.

NICKEL BRIGHTNER 009 / NI BRIGHT
NICKEL SALT531R
NI. ADDITIVE022
NICKEL BRIGHTENER-009
ANTIPIT A (OPTIONAL) / 250-400 G/L
10ML/L
0.3-0.5 ML/L
0.2-0.3 ML/L /
  • Extremely repid rates of brightening and levelling.
  • Very ductile deposits.
  • Deposits are white in colour and pleasing in appearance.
  • Extremely good for barrel plating

ARISTOCRAT BRIGHT NICKEL-003 / NI BRIGHT
NICKEL SALT-531
NI. ADDITIVE 602
ARISTOCRAT BRIGHTNER-003
ANTIPIT A (OPTIONAL)
TEMPERATURE
PH
CATHODE CURRENT DENSITY / 250-400 g/l
6.0-10.0 ml
0.2-0.3 ml/l
0.2-0.4 ml/l
50-65oC
4.0-4.6
2.0-6.0 A/dm2 /
  • A well balancd formulation gives excellent levelling low current density brightness, good throwing power land chrome receptivity.
  • Very fast brightness and levelling properties
  • Suitable for vat and barrel plating.
  • Production proven process
  • Suitable for automatic lines

BRIGHT NICKEL
851 PROCESS / NI. BRIGHT
NICKEL SALT531R
NI. ADDITIVE 850
NI BRIGHTNER 851
ANTIPIT A (OPTIONAL) / 350-400 g/l
6.0-10.0 ml/l
6.0-10.0 ml/l
0.2-0.3 ml/l /
  • A well balancd formulation gives excellent levelling low current density brightness, good throwing power land chrome receptivity.
  • Very fast brightness and levelling properties
  • Suitable for vat and barrel plating.
  • Production proven process

GEMINI BRIGHT NICKEL007 PROCESS / NI. BRIGHT
NICKEL SALT531R
NI.DDITIVE 022
NI.BRIGHTNER 007
ANTIPIT A (OPTIONAL)
TEMPERATURE
PH
CATHODE CURRENT DENSITY / 300-400 g/l
8-10 ML/L
0.2-0.3 ML/L
50-65oC
4.2-4.6
2.0-4.0 A/dm2 /
  • Designed primerly for duplex ni.process where 007 brightner nickel is used for depositing highly levelled ductile deposit over semi bright nickel coating,
  • Very good coverage even at very low c.d. areas
  • Excellent chrome receptivity.

SMART NICKEL
BRIGHTNER V-97 / NI BRIGHT
NICKEL SALT-531R
NI. ADDITIVE 022
SMARTNI.BRIGHTENER.V-97
ANTIPIT A (OPTIONAL) / 250-400 G/L
10ML/L
0.3-0.5 ML/L
0.2-0.3 ML/L /
  • Extremely repaid rates of brightening and levelling.
  • Very ductile deposits.
  • Deposits are white in colour and pleasing in appearance.
  • Extremely good for barrel plating

BRIGHT NICKEL
777 PROCESS / NI. BRIGHT
NICKEL SALT531R
NI. ADDITIVE602
NI.BRIGHTNER 777
ANTIPIT A (OPTIONAL)
TEMPERATURE
PH
CATHODE CURRENT DENSITY / 350-400 g/l
6.0-10.0 ml
0.2-0.3 ml/l
0.2-0.4 ml/l
50-65oC
4.0-4.6
2.0-6.0 A/dm2 /
  • A well balancd formulation gives excellent levelling low current density brightness, good throwing power land chrome receptivity.
  • Very fast brightness and levelling properties
  • Suitable for vat and barrel plating.
  • Production proven process
  • Suitable for automatic lines.

BRIGHT NICKEL
ROLEX-673 PROCESS / NI. BRIGHT
NICKEL SALT531R
NI. ADDITIVE 022
ROLEX-673
BRIGHTENER
ANTIPIT A (OPTIONAL) / 350-400 G/L
8ML/L
0.3-0.5 ML/L
0.2-0.3 ML/L /
  • Extremely rapid rates of brightening and levelling.
  • Very ductile deposits.
  • Deposits are white in colour and pleasing in appearance.
  • Extremely good for barrel plating

SUPER BRIGHT NI.LEVELLER 644 / NI. LEVELLER 644 / 0.2-0.5 ml/l /
  • An addition agent for bright nickel which can be used to impart additional levelling on poorly polished

LUMAX NICKEL
LEVELLER-744 / LUMAX-NICKEL
LEVELLER-744 / 0.2-0.4 ml/l /
  • An exceptional rejuvenating product to improve the levelling and brightness even with nickel solutions contaminated with organic impurities

SEQUESTENT 532 / SEQUESTENT 532 / 0.2-0.8 ml/ll /
  • A purifier for bright nickel solutions to improve tolerance to metallic impurities like disolved copper and zinc.

LCD. EXTENDER 535 SPL. / LCD.EXTENDER
535.SPL / 0.2-0.8 ml/l /
  • An extra-ordinay product which gives high tolerance to metallic impurities like zinc and copper.
  • Eliminates frequent time consuming electrolytic dummying. improves the nickel coverage even at reccessed areas.

NIKO-PURIFIER 535 / NIKO PURIFIER 535 /
  • An insoluble filter media to use in filter packs to remove metallic impurities from nickel plating bath.
  • Regular usage eliminates high ph treatment and electrolytic dummying.

GEMINI BLACK
NICKEL PROCESS / GEMINI BLACK NICKEL SALT
TEMPERATURE
PH
CURRENT DENSITY / 60-100 g/l
30-50oC
5.2-5.8
0.1-1.0 A/dm2 /
  • The process produces pleasing black coloured deposit which has a good decorative appearance.
  • Particularly suitable for components such as camera fittings, optical, electrical instruments, novely jewellery articles and metal name plates..

DUPLEX & TRIPLEX NICKEL

MSBEE SEMI-BRIGHT NICKEL PROCESS / MSBEE SEMI BRIGHT NICKEL SALT
MSBEE.ADDITVE 542
MSBEE.BRIGHTNER 543
PH.
TEMPERATURE
CURRENT DENSITY / 250-450 g/l
8.0-12.0 ml/l
0.8-1.6 ml/l
3.5-4.0
50-60oC
2.0-6.0 A/dm2 /
  • The new msbee semibright nickel process is based on advanced technology designed to produce high corrosion resistant semi bright nickel depost.
  • Ideal for duplex nickel and triplex nickel plating system which has a special advantage providiing milivolt difference more than 110 mv.
  • Production proven process used extensively in fully automatic installations.

NEW MAGIC SEMI BRIGHT NICKEL PROCESS / NEW MAGIC SEMI BRIGHT NICKEL SALT
MAGIC NO.1
MAGIC NO.2
MAGIC NO.3
PH
TEMPERATURE
CURRENT DENSITY / 350-450 g/l
8.0-12.0 ml/l
0.8-1.6 ml/l
0.2- 0.4 ml/l
3.5-4.0
50-60oC
4.2-4.6
3.0-4.0 A/dm2 /
  • New magic semibright nickel process is based on advanced technology designed to produce high corrosion resistant semi bright nickel deposit.
  • Ideal for duplex nickel and triplex nickel plating system which has a special advantage providing milivolt difference more than 120 mv.
  • Production proven process used extensively in fully automatic installations.

SPL. TRI NICKEL PROCESS / SPL NICKEL SALT
SPL.TRI.NICKEL ADDITIVE
TEPERATURE
PH
CURRENT DENSITY / 300-350 g/l
10-20 ml/l
50-60oC
4.2-4.6
3.0-4.0 A/dm2 /
  • Used as an intermediate layer between semibright and bright nickel deposit.
  • Provides high sulphur nickel deposit below the bright nickel to prevent pit type corrosion to the base metal
  • Widely used in fully automatic installations for plating cycle and motor cycle components.

SATIN NICKEL

PEARL SILK NICKEL PROCESS / PEARL SILK NICKEL SALT
PEARLSILK NI. ADDITIVE 045
PEARLSILK NI. ADDITIVE 046
PEARL SILK NI. ADDITIVE 049
PH
DENSITY
TEMPERATURE
CATHODE
CURRENT DENSITY
ANODE C.DENSIT
AGITATION. / 520-550 G/L
15-20 ml/l
6-10 ml/l
0.4 ml/l
4.0-4.3
31-33oBe
50-55oC
4-8A/dm2
1-3A/dm2
CATHODE ROD MOVEMENT /
  • Developed to produce non glaring, silky, stain-free attractive satin nickel deposits
  • Suitable for rack plating only
  • Various satinizing effects can be achieved by varying pearl silk ni additive 049 concentration.
  • Coating gives excellent white finish if followed by mahavir’s ‘white bronze process’

ELECTROLESS NICKEL PROCESS

MINPLATE 618 PROCESS / MINPLATE NI 618A
MINPLATE NI 618B
MINPLATE NI 618C
PH
TEMPERATURE / 60 ml/l
90ml/l
only for replenishment
4.8-5.0
86-92OC /
  • A bright highly stable elctroless nickel system designed to produce hard, corrosion resistant coating having phosphorus content in excess of 7% by weight.

MINPLATE 620 AL / MINPLATE 620 A
MINPLATE 620 B
MINPLATE 620 C
PH
TEMPERATURE / 150 ml/l
70ml/l
only for replenishment
9.6-11.5
34-43OC /
  • Minplate al 620 is an electroless nickel strike bath for processing aluminium prior to electroless nickel or electrolytic nickel plating
  • For make up 620 a and 620 b are used and 620a and 620 c for replenishment

NICKEL-FREE PLATING PROCESS
NIK-FREE PROCESS .

WHITE BRONZE PLATING

WHITE BRONZE PROCESS: / WHITE BRONZE
SOLUTION
TEMP
VOTAGE
ANODE
PLATING TIME / FULL STRENGTH
ROOM-
S.S 316
FLASH TO 5 MIN(as required finish) / A unique product developed at mahavir
For the market requirement of nickel free silvery white finish.
Excellent result over brass, copper base metals directly,
Superb finish over nickel and satin nickel plating on Wwatch cases, ball pen
Key-chain, belt and hard ware items
Can be used as an alternate of tin plating as deposit has Very good soldering property, can be used for pcb.’s also.
YELLOW BRONZE SOLUTION / CONCENTRATION
VOLTAGE
TEMP
PLATING TIME
ANODE / FULL STRENGTH.
3 TO 5
60C
3 TO 10 MIN
S.S 316 / A unique product developed at mahavir for the market requirement for nickel free yellow finish, can be used as undercoat of gold plating to increase the life of uppercoat of flash gold, the deposits are having very good antitarnishing porperties,

CHROME PLATING PROCESS

REGULAR CHROME
PROCESS / REGULAR CHROME SALT
BRIGHT CHROME
CONDUCTING SALT
TEMPERATURE
CURRENT DENSITY / HARD DECORATIVE
230-250 g/l 300-350 g/l.
5-15 g/l 5-10 g/l
55-60OC 40-50OC
15-30 A/DM2 15-25 A/DM2 /
  • Designed for both hard and decorative chromium plating by varying the concentration and operating conditions
  • Conventional type process and very easy to maintain

SUPER SPEED
CHROME SALT- 314 / SUPER SPEED
CHROME SALT-314
SUPER SPEED
CONDUCTING SALT317
TEMPERATURE
CURRENT DENSITY / 250 g/ll
6.0-14.0 g/l
55-65OC
15-35 A/dM2 /
  • A high speed chrome bath which employs a special mixed soluble catalyst, meets the modern requirements of hard and bright chrome.
  • A self regulating chrome process.
  • Better covering and throwing power than conventional chrome.

S.S.N.E HARD CHROME PROCESS / SSNE HARD CHROME SALT
SSNE ADDITIVE NO.1
SSNE ADDITIVE NO.2
DENSITY
TEMPERATURE
CURRENT DENSITY / 250-350 g/l
10-20 ml/l
15-20ml/l
22-28OBe
50-60OC
10-40 A/dM2 /
  • Produces deposit s with a hardness of approximately 1050 vickers. higher current efficiency than conventional chrome.
  • No attack on base metal and hence suitable for internal plating of cylinder liners.

SUPER SPEED 319-L / SUPER SPEED 319-L / 10-30 ML/L /
  • A liquid catalyst for high speed hard chrome plating specially recommended to improve the current efficiency, brightness and hardness.
  • Good correction additive in used chrome solution.

MAHA-ACT
NI.ACTIVATOR / MAHA-ACT
TEMPERATURE
TIME
CATHODE CURRENT
DENSITY / 10ML/L.
ROOM
10-60 SECS.
0.01-0.0A/dm2 /
  • A very good activating bath prior to normal chrome bath to activate the passive bright nickel.
  • Eliminates completely the white patch problem in subsequent chrome deposits.
  • Bath has such low concentration and hence can be discarded at regular intervals to have troublefree operation.

MARWELL CHEOME
MCD / MARWELL CHROME MAKE UP SALT
MARWELL-MCD
MAKE UP SOLUTION
TEMPERATURE
CATHODE
CURRENT DENSITY
VOLTAGE / 250 G/L
20 ml/l
50-60OC
20-60 A/dm2
8V-12 VOLTS /
  • Suitable for internal plating of diesel engine cylinders.
  • Higher efficiency, higher hardness upto 1100 vpn
  • No anode corrosion
  • Very smooth and bright deposits
  • Micro crack deposits greater than 40 cracks/mm.
  • Higher current efficiency (23-26%)

MISTCONTROLER
307-S / MISCONTROLER 307S / 0.75-1.0 g/l /
  • Fume reducer for all types of chrome plating baths to suppress the fumes
  • Provides good foam blanket.

MISTCONTROL
307-L / MISTCONTROL
307-L / 1.0-2.0 ML/L /
  • Specially recommended for hard chrome plating baths to suppress the fumes

BLACK CHROME
PROCESS. / BLACK CHROME SALT
BLACK CHROME ADDITIVE
TEMPERATURE
CURRENT DENSITY / 300-400 g/l
8-10 g/l
18-25OC
30-40 A/dm2 /
  • Black chrome deposits with high corrosion resistance for functional & decorative application. good thermal stability and hence can be used for high temperature applications.
  • Good process for plating solar panels.

CHROME NEUTRALIZER 306 / CHROME NEUT.306 / 50g/l / Hexavalent chromium neutralizer, used after plating to remove chrome traces from chromium plated components.
TIN-COBALT PROCESS(CHROMELIKE)
ROBIN-BLUE
PROCESS / ROBIN-BLUE
STARTER
ROBIN BLUE
MAKE-UP
CATHODE CURRENT
DENSITY
TEMPERATURE
PH
PLATING TIME
ANODE
AGITATION / 250 ml/l
40-60 ml/l
0.2-1.0 A/dm2
45-55o C
8.5-9.0
1-4Mins.
CARBON OR TIN PLATE
CATHODE ROD MOVEMNET /
  • Bright deposits colour resembles chrome colour.
  • Excellent covering power & thus suitable for barrel plating.
  • Does not contain any toxic material & easy for waste treatment.

ZINC PLATING PROCESS
CYANIDE ZINC PLATING PROCESS
BRILLIANTG CZ 265 BRIGHTENER / CYN. ZINCSALT 201