REPORT FOR HOT GALVANIZING

/ Form No: /

D.105

Page: / 1 of 2
Issued: / 020121
Rev: / 131231
Report No: / Part of I-pl. No: / Sign:
Product Supplier / Galvanizing Company
Plant / Dispatch note No: / Order No:
Delivery note No:
Directions treatm. type acc. to
TBY or standard / System / Component/Object / Drawing No:
Remaining information / Inspection moment KBM EP
MANUFACTURE INSPECTION ACC. TO SS-EN ISO 1461:2009. edition 2 / SELECTION OF SAMPLES ACC. TO SECTION 5, SS-EN ISO 1461:2009, edition.2 YES NO / No of test-pieces
MEASURED MEDIUM-
COAT THICKNESS / Coat weight acc. to table 3 / PRODUCT WITH NOMINAL THICKNESS WHICH ARE NOT CENTRIFUGED
Steel t ³ 6 / Steel 3 £ t < 6 / Steel 1,5 £ t < 3 / Steel t < 1,5 / Casting
³ 6 / < 6
Min. local coat / Min. mean value / Min. local coat / Min. mean value / Min. local coat / Min. mean value / Min. local coat / Min. mean value / Min. local coat / Min. mean value / Min. local coat / Min. mean value
MEASURED MEDIUM-
COAT THICKNESS / Coat weight acc. to table NA.1 / PRODUCT WITH NOMINAL THICKNESS WHICH ARE NOT CENTRIFUGED
Steel t ³ 6 / Steel 3 £ t 6 / Steel 1 £ t 3
Min. local coat / Min. mean value / Min. local coat / Min. mean value / Min. local coat / Min. mean value
Fe / Zn 115
Fe / Zn 165
Fe / Zn 215
MEASURED MEDIUM-
COAT THICKNESS / Coat weight acc. to table D.4 / PRODUCT WITH NOMINAL THICKNESS WHICH ARE CENTRIFUGED
³ 6 mm
diameter / ³ 6 mm diameter / Steel t ≥ 3 mm / Steel t< 3 mm
Min. local coat / Min. mean value / Min. local coat / Min. mean value / Min. local coat / Min. mean value / Min. local coat / Min. mean value
Threaded objects
Other objects incl. casting
Inspection that the surface is free from
visible defaults
acc. to section 6 / Blips / Fluxmedium-
remains and
zinc ash / Blister / Holiday
Lumps and
thick runnings / Drops / Holidays are £ 0. 5% of the total area
No requirement about galvanising
Proposal for action or other information
Testing according to specific requirements i.e painting: YES NO
Above mentioned inspection has been done and the galvanizing fulfill the specific requirements.
Date: Name: