Batteryspace.com
PRODUCT SPECIFICATION
TY Model: MH-2/3A1100P
Document Number:TY/20030409
1. PREFACE
This specification applies to the Nickel-Metal Hydride Cylindrical batteries or battery packs. Batteryspace reserves the right to alter the product design or amend this specification without prior notice.
2. RATINGS
Description / Unit / Specification / ConditionsNominal Voltage / V / 1.2 / unit cell
Nominal Capacity / mAh / 1,000 / Standard Charge/Discharge
Typical Capacity / mAh / 1,100 / Standard Charge/Discharge
Standard Charge / mA / 100(0.1C) / Ta=0～40℃
hour / 16.
Fast Charge / mA / 500(0.5C) / dT/dt=0.5～1℃/min.
-△V=0～5mV/cell
Timer Cutoff=105% Nominal capacity
Temp. Cutoff=40-45℃
Ta=10～35℃
hour / 2.2(approx. see note2)
Trickle Charge / mA / 45(0.05C)～100(0.1C) / Ta=0～40℃
Discharge Current / mA / 100(0.1C) ～3,000(3C) / Ta=-20～50℃
Discharge Cut-off Voltage / V/cell / 1.0
Storage Temperature / ℃ / -20～35℃
Typical Weight (unit cell) / gram / 20(approx.)
3.PERFORMANCE
Unless otherwise stated, tests should be done within one month of delivery under the following conditions.
Ambient Temperature: Ta = 20±5℃ and
Relative Humidity: 65±10%
Notes:
Standard Charge/Discharge Conditions
Charge: 100mA(0.1C)x16hours
Discharge: 200mA(0.2C)to 1.0V/cell
Test / Unit / Specification / Conditions / RemarksCapacity / mAh / ≥1,000 / Standard Charge, rest no more than 1hour, Standard Discharge / Up to 3 cycles allowed
Open Circuit
Voltage(OCV) / V/cell / ≥1.25 / Within 14 days after standard charge
Internal
Impedance / mΩ/cell / ≤11 / Upon fully charge(1KHz)
High Rate
Discharge(1C) / minute / ≥54 / Standard Charge, no more than 1hour rest before discharge
High Rate
Discharge(10C) / minute / ≥5.5 / Standard Charge, no more than 1hour rest before discharge, Discharge Cut-off Voltage 0.8V / Mid-Point Voltage ≥0.9V
Overcharge / No leakage, no explosion / 100mA(0.1C)Charge 1 year
Charge
Retention / mAh / ≥700 / Standard Charge ,
Storage 28days,
Standard Discharge
Low Temperature Performance / minute / ≥36 / Standard Charge(20±5℃), rest less than 2hrs then 1C discharge to 1.0V/cell at 0±2℃
IEC Cycle Life / Cycle / >500 / IEC285(1993)4.4.1 / (see Note 3)
Short
Circuit / Leakage＆deformation may occur, but no explosion is allowed. / After standard charge,
short circuit for 1hr(leading wire=0.75mm2x20mm)
Vibration
Resistance / Change of voltage should be under 0.02V/cell, / Charge the battery 0.1C 16hrs,then leave for 24hrs, check battery before/after vibration,
Amplitude 4mm
Vibration 1000 CPM
Any direction for 60mins
Impact
Resistance / Change of voltage should be under 0.02V/cell, / Charge the battery 0.1C 16hrs, then leave for 24hrs ,check battery before/after dropped ,
Height 45cm
Wooden board (thickness 30mm)
Direction not specified, 3 times
4. CONFIGURATION AND DIMENSIONS
Please refer to the attached drawing.
5. EXTERNAL APPEARANCE
The battery shall be free from cracks, scars, breakage, rust, discoloration , leakage nor deformation.
6. WARRANTY
Batteryspace will be responsible for replacing the battery against any defects or poor workmanship for one (1) year from the date of shipping.
Any other problems caused by malfunction of the equipment or misuse of the battery is not under this warranty.
7. CAUTION
1. Reverse charging is not acceptable.
2. Do not charge/discharge with more than specified current.
3. Do not short circuit the cell/battery. Permanent damage to the cell/battery may result.
4. Do not incinerate or mutilate the cell/battery.
5. Do not solder directly to the cell/battery.
6. The life expectancy may be reduced if the cell/battery is subjected to adverse conditions like, extreme temperature, deep cycling, excessive overcharge/ over discharge.
7. Store the battery uncharged in a cool dry place. Always discharge batteries before bulk storage or shipment.
8. SAFETY
To assure safety, please consult with the batteryspace technical staff about your applications, including electrical specifications, mechanical designs, protection devices and any special specification.
Note:
1. Ta: ambient temperature.
2. Approximate time from discharged state. For reference only.
3. IEC285 (1993) 4.4.1Cycle Life.
Cycle No . / Charge / Rest / Discharge1 / 0.1Cx16h / none / 0.25Cx2h20min
2-48 / 0.25Cx3h10min / none / 0.25Cx2h20min
49 / 0.25Cx3h10min / none / 0.25Cto1.0V/cell
50 / 0.1Cx16h / 1-4h / 0.2Cto1.0V/cell
Cycles 1 to 50 shall be repeated until the discharge duration on any 50th cycle becomes less than 3hrs .
3 / CELL / 1 / MODEL / TH-29A100T
2 / TUBE / 1 / P.V.C
1 / INSULATING RING / 1 / PAPER
No. / DRAWING No / PART NAME / Q`TY / MATERIAL / REMARK
DRAW / WANG YU JIE / UNIT / Q`TY / WEIGHT
CHECK / (mm) / 1 / ABOUT 20g
DESIGN / SCALE / DATE / 08/20/03
DRAW No. / Q/TY003100