Chapter 4 Problems
2. Use equations 4.4 [] and 4.10 [] to estimate the number of crystal-like clusters in 1 mm3 of copper at its melting point for spherical clusters containing (a) 10 atoms, (b) 60 atoms. What volume of liquid copper is likely to contain one cluster of 100 atoms? The atomic volume of liquid copper is 1.6´10-29 m3, gSL is 0.177 J/m2, k = 1.38´10-23 J/K, Tm = 1356 K.
4. Calculate the homogeneous nucleation rate in liquid copper at undercoolings of 180, 200 and 220 K, using the following data: L = 1.88´109 J/m3, Tm = 1356 K, gSL = 0.177 J/m2, f0 = 1011 s-1, C0 = 6´1028 atoms/m3, k = 1.38´10-23 J/K.
6. Show that Equation 4.16 [] follows from 4.15 () using the following relationships for a spherical cap: , , and .
10. (a) Show that surface melting is to be expected below Tm in gold (1336 K) given gSL = 0.132, gLV = 1.128, gSV = 1.400 J/m2.
(b) Given that the latent heat of fusion of gold is 1.2´109 J/m3 estimate whether sensible liquid layer thickness are feasible at measurably lower temperature than Tm.
14. Show that Equation 4.35 {} satisfies 4.34 [].
15. The Al-Cu phase diagram is similar to that shown in Fig. 4.19 with Tm(Al) = 660°C, TE = 548°C, Xmax = 5.65 wt%, and XE = 33 wt% Cu. The diffusion coefficient for the liquid DL = 3´10-9 m2/s. If an Al-0.5 wt% Cu alloy is solidifies with no convection and a planar solid/liquid interface at 5 mm/s:
(a) What is the interface temperature in the steady state?
(b) What is the thickness of the diffusion layer?
(c) What temperature gradient will be required to maintain a planar interface?
(d) Answer (a), (b) and (c) for an Al-2 wt% Cu alloy solidified under the same conditions.
16. (a) Using Equation 4.33 [] and the data in problem 4.15 plot the variation of copper concentration along a unidirectionally solidified bar of an Al-2 wt% Cu alloy assuming no diffusion in the solid and perfect mixing in the liquid.
(b) What fraction of the bar will solidify to a eutectic structure?
(c) How much eutectic would form in an Al-0.5 wt% Cu alloy solidified under the same conditions?
19. Show that the condition gives (i) the maximum eutectic growth rate for a given undercooling, and (ii) a minimum undercooling for a given growth rate (Equation 4.43: ).
20. Calculate the depression of the eutectic temperature for a lamellar eutectic with r = 0.2 mm and r = 1.0 mm, if gab = 400 mJ/m2, DH/Vm = 800´106 mJ/m3, TE = 1000 K.
21. If it is assumed that the choice of a rod or lamellar eutectic is governed by the minimization of the total a/b interfacial energy it can be shown that for a given l there is a critical volume fraction of the b phase (fc) below which b should be rod like, and above which it should be lamellar. Assuming the rods are hexagonally arranged and that gab is isotropic, calculate the value of fc.